Warning: fopen(/home/virtual/kwjs/journal/upload/ip_log/ip_log_2024-03.txt): failed to open stream: Permission denied in /home/virtual/lib/view_data.php on line 88 Warning: fwrite() expects parameter 1 to be resource, boolean given in /home/virtual/lib/view_data.php on line 89 Evaluation of HIC Resistance for Thick-wall Welded Pipe

Journal of KWJS 2005;23(3):34-39.
Published online July 15, 2005.
[기술논문]후육 용접 강관의 HIC 저항성 평가
, ,
 
Evaluation of HIC Resistance for Thick-wall Welded Pipe
JunSeok Seo, HeeJin Kim, Hoi-Soo Ryoo
Abstract
It is required for the steel used in the sour environment to have sufficient to hydrogen induced cracking(HIC). For pipe steels, HIC resistance could be varied during making process due to the large plastic deformation applied in the thick-wall pipe. In order to figure out such effect, HIC tests were performed not only in the plate condition but in the pipe condition and their results were compared in terms of cracking ratio. Test results demonstrated a detreimental effect of plastic deformation to HIC resulting in a substantial in the cracking ratio after pipe forming process. All of the cracks found in the pipe material were located in the outer of pipe where the tensile was resulted during pipe forming stage. In order to understand HIC resistance of the pipe but in the plate condition, it was suggested to pre-strain the plate to some extent before the HIC test.


ABOUT
BROWSE ARTICLES
ARTICLE CATEGORY 
FOR CONTRIBUTORS
Editorial Office
#304, San-Jeong Building, 23, Gukhoe-daero 66-gil, Yeongdeungpo-gu, Seoul 07237, Korea
Tel: +82-2-538-6511    Fax: +82-2-538-6510    E-mail: koweld@kwjs.or.kr                

Copyright © 2024 by The Korean Welding and Joining Society.

Developed in M2PI